Series CFT forced convection flat tempering furnace is the basic type of glass tempering furnace which has been widely accepted by overseas customers. Firmly upholding the philosophy of "the pursuit of excellence”, the series CFT forced convection flat tempering furnace adopts imported motor and accessories to ensure its good quality. Besides, draught fan can provide a circulating heat flow inside the machine to keep a full uniform heat. With higher capacity than radiation flat tempering furnace, it is more suitable for processing Low-e tempered glass for construction furniture industry.
Features
1. Shanghai Glass Machinery is an ISO and CE accredited forced convection flat tempering furnace supplier in China. It has obtained a patent on invention; the patent number is 102008025795.
<1> Overall flatness deviation<1.5mm/1000mm
<2> Local flatness deviation<0.1mm/300mm
<3> Granularity is strictly according to DIN EN 12150 standard(>=40pieces in 50×50mm)
<4> No visible scratches or marks on surface.
2. Shanghai Glass Machinery has long-term cooperation with many universities and scientific research institutions.
3. Monitoring data is provided during the productive process.
4. We provide customized service and installation training service for large production line.
Application
The machine is used for making flat tempered glass.
Parameter
|
Type
|
Max.
Glass size
|
Min.
Glass size
|
Glass
thickness
|
Capacity
|
Heating
Power
|
Installed
Power
|
|
m x
m
|
m x
m
|
mm
|
M²/h
|
kw
|
kw
|
|
CFT1525
|
1.5x2.5
|
0.15x0.3
|
4~19
|
57
|
288
|
448
|
|
CFT1530
|
1.5x3
|
|
|
68
|
345
|
507
|
|
CFT1536
|
1.5x3.6
|
82
|
403
|
593
|
|
CFT1830
|
1.8x3
|
82
|
410
|
640
|
|
CFT1836
|
1.8x3.6
|
98
|
479
|
709
|
|
CFT2030
|
2x3
|
91
|
453
|
683
|
|
CFT2036
|
2x3.6
|
109
|
529
|
779
|
|
CFT2042
|
2x4.2
|
127
|
605
|
885
|
|
CFT2436
|
2.4x3.6
|
131
|
630
|
910
|
|
CFT2442
|
2.4x4.2
|
153
|
720
|
1030
|
|
CFT2448
|
2.4x4.8
|
175
|
810
|
1120
|
|
CFT2454
|
2.4x5.4
|
197
|
900
|
1245
|
|
CFT2460
|
2.4x6
|
219
|
990
|
1420
|
|
Glass Type
|
Clear Float Glass
|
Low-E
E=0.07
|
Low-E
E=0.03
|
|
Glass thickness(mm)
|
4
|
5
|
6
|
8
|
10
|
12
|
15
|
19
|
6
|
6
|
|
Unit Heating Tine(s/mm)
|
28
|
30
|
30
|
32
|
36
|
40
|
45
|
50
|
40
|
50
|
|
Capacity(1/h)
|
22
|
20
|
17
|
12.7
|
9
|
7
|
5
|
3.5
|
12
|
10
|
|
Energy Consumption(kw.h/m2)
|
3.5
|
3.5
|
3.6
|
4.8
|
5.7
|
7.0
|
8.0
|
10
|
5.2
|
5.3
|
|
Overall Bow≤(%)
|
1.2
|
1.0
|
1.0
|
1.0
|
1.0
|
0.8
|
0.8
|
1.2
|
1.2
|
1.2
|
|
Local Bow≤(%)
|
0.40
|
0.35
|
0.35
|
0.30
|
0.30
|
0.30
|
0.30
|
0.30
|
0.35
|
0.40
|
|
Wind spots
|
Can not be observed
with naked eyes under the conditions of: A .The total stacked glass thickness
is no more than 20mm. B. The glancing angle is no less than 150.
|
Note: This parameter is the general type; we provide customized service for special requirements.